Made from Aramid fibre, Mineral fibre &
Inorganic bounded with NBR Elastomers
Applications:
This material Contains high amount of mineral fibre
whcih is bi-soluble and thus does not pose any health
hazard. It does not contain any material which might
contribute to bacterial or fungal growth. It is used in
food grade/ drug applications.
THICKNESS
:
0.25 mm to 6.00 mm. (OTHER THICKNESS ON REQUEST)
COLORS
:
GREEN
DIMENSION OF SHEETS
:
1500MM X 1500MM, 1500MM X 3100MM, 1500MM X 1000MM,
1500MM X 2000MM, 1270MM X 1270MM, 1270MM X 3810MM, 3000MM
X 3000MM
OPERATING CONDITION
:
Maximum Peak Temp. : 400°C
Maximum pressure : 150 BAR
Maximum Temperature : 100°C
The following Information Applies to
material Thickness 1.5MM
S.NO.
Typical Properties
Test Method
Unit
Specified Value
1
DENSITY
----------
Gm / cm3
1.70 - 2.00
2
TENSILE STRENGTH
a) ACC to ASTM F152
(ACROSS GRAIN)
N/MM2
7 Min.
b) ACC to DIN52910
(ACROSS GRAIN)
N/MM2
5 Min.
3
COMPRESSIBILITY
ASTM F36A
%
7 – 15
4
RECOVERY
ASTM F36A
%
³ 50
5
FLUID ABSORPTION
(a) IN ASTM OIL NO. 3
ASTM F 146
INCREASE IN MASS
%
15
INCREASE IN THICKNESS
%
10
(b) IN FUEL B
ASTM F 146
INCREASE IN MASS
%
10
INCREASE IN THICKNESS
%
10
(c) IN WATER/ANTIFREEZE
ASTM F 146
INCREASE IN MASS
%
15
INCREASE IN THICKNESS
%
5
6.
IGNITION LOSS
DIN 5291
%
≤28
7.
SEALABILITY AGAINST NITROGEN
DIN 3535
Cm3/min.
≤1.00
8.
STRESS RESISTANCE
16h 300C
DIN 52913
N/mm2
~20
16h 175C
DIN 52913
N/mm2
~28
NOTE
All information and recommendations given
in this brochure are correct to the best of our knowledge.
However, in view of the wide varsity of possible installation
and operating conditions one cannot draw the final conclusion in
all application cases regarding the behaviour in a gasket joint.
Therefore, information can only serve as a guideline.