Hypersil HNA 700 C. F.
 
Aramid Fibre, Carbon Fibre, NBR.
  • For mediium to higher loadings.
  • Excellent for steam & Alkalies
  • Chemical & petrochemical industries.
  • Pulp, Paper, chemical & petrochemical industries.

 
 
 
Density g / cm3
:
1.70-2.00
Tensile Strength N/MM2
Acc to ASTM F 152 (Across Grain)
:
> 8
Acc to DIN 52910 (Across Grain)
:
> -
Compressibility ASTM F 36A %
:
7-12
Recovery ASTM F 36A %
:
> 50
Fluid Absorption
In ASTM Oil No.3 ASTM F 146 %
Increase in Mass
:
< 10
Increase in Thickness
:
< 8
In Fuel B ASTM F 146 %
Increase in Mass
:
< 10
Increase in Thickness
:
< 7
In water / Antifreeze ASTM F 146 %
Increase in Mass
:
< 10
Increase in Thickness
:
< 7
In Acid (Change in Tensile Strength)
96% H2SO2ACID (48 hrs. At 23 .C)
95% HNO3ACID (48 hrs. At 23 .C)
Ignition Loss DIN 52911 %
:
< 30
Sealability Against Nitrogen DIN 3535 Cm3 / min
:
< 0.5
Stress Resistance
16h 300.C DIN 52913 N/mm2
:
~ 20
16th 175.C DIN 52913 N/mm2
:
~ 30
Design Info
M value
:
2.5
Y value (mpa)
:
22
Max. Peak Temp..C
:
450
Max. Continous Temp. .C
:
350
Max. Operating Pressure Kg/cm2
:
100
ASTM F 104 Line call-out
:
-