| Density g / cm3 |
: |
1.70-2.00 |
| Tensile
Strength N/MM2 |
| Acc to ASTM F 152
(Across Grain) |
: |
> 14 |
| Acc to DIN 52910
(Across Grain) |
: |
> 11 |
| Compressibility ASTM
F 36A % |
: |
6-12 |
| Recovery ASTM F 36A
% |
: |
> 50 |
| Fluid
Absorption |
| In ASTM
Oil No.3 ASTM F 146 % |
| Increase in Mass
|
: |
< 10 |
| Increase in
Thickness |
: |
< 8 |
| In Fuel
B ASTM F 146 % |
| Increase in Mass
|
: |
< 10 |
| Increase in
Thickness |
: |
< 7 |
| In water
/ Antifreeze ASTM F 146 % |
| Increase in Mass
|
: |
< 15 |
| Increase in
Thickness |
: |
< 5 |
| In Acid
(Change in Tensile Strength) |
| 96% H2SO2ACID
(48 hrs. At 23 .C) |
| 95% HNO3ACID
(48 hrs. At 23 .C) |
| Ignition Loss DIN
52911 % |
: |
< 30 |
| Sealability Against
Nitrogen DIN 3535 Cm3 / min |
: |
< 0.5 |
| Stress
Resistance |
| 16h 300.C
DIN 52913 N/mm2 |
: |
~ 25 |
| 16th 175.C
DIN 52913 N/mm2 |
: |
~ 36 |
| Design
Info |
| M value |
: |
2.5 |
| Y value (mpa) |
: |
20 |
| Max. Peak Temp..C
|
: |
500 |
| Max. Continous Temp.
.C |
: |
350 |
| Max. Operating
Pressure Kg/cm2 |
: |
150 |
| ASTM F 104 Line
call-out |
: |
F712112A9B4E12M4 |