| CJ - 43 |
| |
| Asbestos Gasket Jointing Sheet Without Wire |
|
 |
| Material Composition: |
| Made from Chrysotite Asbestos
Fiber with Synthetic Elastomers and Inorganic fillers. |
| |
| Applications: |
| To seal of aggressive organic
acids alkalies, alcohals, easters , ketones ,diluted
acids, solvents, mineral oils and thermal oils under
high stress conditions. |
| |
| |
|
 |
|
| |
| THICKNESS
|
: |
0..25, 0.5mm, 0.8mm, 1mm, 1.5mm, 2mm, 3mm,
4mm, 5mmm , 6mm (OTHER THICKNESS ON REQUEST) |
| SURFACE FINISH |
: |
Grey , Graphited (OTHER COLORS ON
REQUEST) |
| DIMESNSION OF SHEETS |
: |
1500MM X3100MM, 1500MM X1500MM, 1500MM X
1000MM, 1500MM X 2000MM, 1270MM X1270MM, 1270MM X 3810MM,
3000MM X 3000MM |
| OPERATING CONDITION |
: |
Maximum pressure : 200
BarTemperature: 550°C |
| SPECIFICATION COMPLIANCE
|
: |
ISI : 2712 / 1998 Grade O / 1, W / 1 |
|
| |
| The following Information Applies to
material Thickness 1.5mm. |
| |
| S.NO. |
Typical Properties |
Test Method |
Unit |
Specified Value |
|
1 |
Density |
IS:2712/1998 |
g /cm3 |
1.70 - 2.20 |
|
2 |
Tensile Strength |
IS:2712/1998 |
Mpa |
>26.0 |
|
3 |
Compressibility |
IS:2712/1998 |
% |
6 – 14 |
|
4 |
Recovery |
IS:2712/1998 |
% |
>40 |
|
5 |
Ignition Loss |
IS:2712/1998 |
% |
<28 |
|
6 |
Stress Resistance |
IS:6210/1979 |
Mpa |
>23 |
|
7 |
FLUID
ABSORPTION |
|
|
|
|
|
IN ASTM OIL NO.3 |
|
|
|
|
|
(a) Thickness Increase |
IS:2712/1998 |
% |
<20 |
|
|
(b) Mass Increase |
IS:2712/1998 |
% |
<15 |
|
|
IN FUEL B |
|
|
|
|
|
(a)Thickness Increase |
IS:2712/1998 |
% |
<15 |
|
|
(b)Mass - Increase |
IS:2712/1998 |
% |
<15 |
|
|
| NOTE |
| All information and recommendations given
in this brochure are correct to the best of our knowledge.
However, in view of the wide varsity of possible installation
and operating conditions one cannot draw the final conclusion in
all application cases regarding the behaviour in a gasket joint.
Therefore, information can only serve as a guideline. |
| |
|
|
|
|